Low-lead brass rods -H65 brass tube - leaded brass capillary brass electrode main purpose is to improve machinability and improved abrasion resistance, impact of lead on the strength of brass. Manganese brass has good mechanical properties, thermal stability and corrosion resistance; Alcan in manganese brass, you can also improve its performance, the smooth surface of the casting. Brass casting and pressure processing can be divided into two types of products. Complete product specifications, price, packaging intact, pure copper, good linearity, inventories, provide material proof and SGS report. Professional production and sales: brass band, brass rods, brass, brass sleeve, yellow copper, brass row, brass wire, copper [Tel: 0769-85317866 Website: www.dg316bxg.com phone: 13725715788 QQ online: 1397644622] Material: H62, H62, H63, H65, H68, H70, H80, H85, H90, H96, T1, T2, C1100, C5111, C5101, C5191, C5210, TU1, TP1, TP2, TAG0. 08, Tag0.1, C1100, C1020, C1201, C1220, C1271, C2100, C2200, C2300, C2400, C2600, C2680, C2700, C2720, C2800, C2801 and so on. Specifications: Thickness: 0.01-2.0mm, width: 305-600mm. Hardness: o, 1 / 2h, 3 / 4h, h, eh, sh like. Copper alloy calculated copper weight (kg) = Thickness (mm) * Width (m) * Length (m) * 8.6 brass weight (kg) = (OD - Wall Thickness) (mm) * wall thickness (mm) * 0.027 copper weight (kg) = Diameter (mm) * Diameter (mm) * 0.0067 Features Introduction: It is a brass alloy composed of copper and zinc. When the amount is less than 39% zinc, zinc can be dissolved within a single phase composed of copper, said the single-phase brass, plastic, suitable for hot and cold pressure processing. When zinc is greater than 39% when there is a single-phase as well as in b copper and zinc-based solid solution, called duplex brass, b and the tensile strength of the plastic small rise, if only for thermal pressure processing continued to add zinc The mass fraction, the tensile strength decreased, no use value code with "H + number" show, H show brass, copper figures show that the mass fraction. H68 show as copper content of 68%, 32% zinc, brass, cast brass in front codenamed "Z" word, such as Zcuzn38 show ZH62 zinc content of 38%, the balance being copper cast brass. H90, H80 single-phase, golden yellow, it has a total gold Moreover, he called plating, decorations, medals and so on. H68, H59 attributed duplex brass, is widely used in structural parts on appliances, such as bolts, nuts, washers, springs, etc. stretch. Typically, cold deformation with single-phase brass hot deformation processing phase brass. Brass is an alloy of copper and zinc. The simplest brass is copper - zinc binary alloy, known as a simple brass or ordinary brass. Change the content of zinc in the brass can be different mechanical properties of brass. The higher levels of zinc in brass, its intensity is higher, lower plasticity. Brass zinc industry used does not exceed 45%, the high zinc content will be brittle, the alloy performance deterioration. In order to improve the performance of a brass, adding other alloying elements on the basis of one dollar brass on brass called special brass. Common alloying elements silicon, aluminum, tin, lead, manganese, iron and nickel. Alcan in brass brass can increase the yield strength and corrosion resistance, slightly lower plasticity. Less than 4% of aluminum-containing brass has good processing, casting and other overall performance. In seawater, and the ability of anti-brass plus 1% tin can significantly improve the marine atmospheric corrosion of brass, so called "Navy brass." Tin can improve cutting performance of brass. Purpose: to do all kinds of deep drawing and bending manufacturing force components, such as pins, rivets, washers, catheters, barometer, screen, radiator parts. Has good mechanical properties, thermal state plastic, plastic is acceptable under cold, machinability, easy fiber welding and welding, corrosion resistance, is widely used an ordinary brass varieties.